| LIDA CPVC rigid sheets CPVC-S series |
| Sizes |
Thickness range: 1mm~30mm Width: 1000mm~1300mm (for thk.1mm~3mm) 1000mm~1500mm (for thk.4mm~20mm) 1000mm~1300mm (for thk.25mm~30mm) Length: Any length. |
| Surface | Glossy, matt, embossed (can make the exact patterns according to customers' requirements.) |
| Standard Colors |
Dark grey(RAL7011), light grey, black, white, blue, green, red and any other colors according to customers' requirements. |
| Characteristics | Excellent chemical and corrosion resistance; Excellent thermo-stability performance; Easily to fabricate, weld or machine High rigidity and superior strength; Reliable electrical insulation; Low flammability, self-extinguishing |
| Applications | Mainly used in the chemical industry for electrolysis, electroplating, paper industry, semiconductors industry and clean-room technology, such as Lab equipments, Etching equipments, Semiconductor processing equipments, chemical storing tanks, oil tanks, storing tanks for brewing water, acid or alkali production towers, acid or alkali washing towers and so on. . |
| Standard sizes | ||||
| Thickness | 1220mm×2440mm | 1500mm×3000mm | 1300mm×2000mm | 1000mm×2000mm |
| 1mm~1.5mm | √ | √ | ||
| 2mm~3mm | √ | √ | √ | |
| 4mm~20mm | √ | √ | √ | √ |
| 25mm~30mm | √ | √ | √ | |
| We can also provide any other sizes according to your special needs. | ||||
| Test Standard (GB/T 22789.1-2008) | Unit | Typical Value | |
| Physical | |||
| Density | 1.45~1.5 | g/cm3 | 1.45 |
| Mechanical | |||
| Tensile Strength(Length/Breadth) | ≥45 | Mpa | 52.9/48.9 |
| Elongation (Length/Breadth) | ≥8 | % | 29/32 |
| Notch Impact Strength (Length/Breadth) |
≥5 | KJ/m2 | 7.83/7.57 |
| Charpy unnotched Impact Strength 0ºC -20ºC |
----- ----- |
KJ/m2 KJ/m2 |
pendulum 4J Sample not break |
| Bending Strength V=2mm/min | ----- | Mpa | 76.2 |
| Ball Indentation Hardness 358N (h: 0.118~0.138) |
----- | N/m | 221 |
| Thermal | |||
| Vicat Softening Temperature | ≥110 | °C | 110.3 |
| Heat Shrinkage (Length/Breadth) | -4~+4 | % | +1.9/-0.1 |
| Chemical | |||
| 35%±1% (v/v) HCI 5h 60°C | ±1 | g/ cm3 | -0.9 |
| 30%±1% (v/v) H2SO4 5h 60°C | ±1 | g/ cm3 | -0.9 |
| 40%±1% (v/v) HNO 5h 60°C | ±1 | g/ cm3 | -0.9 |
| 40%±1% (v/v) NaOH 5h 60°C | ±1 | g/ cm3 | -0.7 |
){kind=link}